Polvos metálicos esféricos GH5188 Polvo de aleación de alta temperatura a base de cobalto

Carácter del producto GH5188 is a solid solution strengthened cobalt based high-temperature alloy, which is strengthened by adding 14% tungsten to give the alloy excellent high-temperature thermal strength. At the same time, adding a high content of chromium and trace amounts of La gives the alloy good high-temperature oxidation resistance. Compared to nickel based high-temperature alloys, GH5188 has more good creep resistance, thermal corrosion resistance, fatigue resistance, and high temperature strength. GH5188 has excellent formability, welding and other process properties, making it suitable for manufacturing parts for aircraft engines that require high strength below 980 ℃ and anti-oxidation below 1000 ℃. In the 1980s, GH5188 alloy was applied to components such as vortex plates and flame deflectors in turboshaft eight aircraft engines. Currently, some aircraft engines use GH5188 alloy sheets to prepare high-temperature components such as combustion chamber walls, outer walls, and sealing plates.   2.Especificación GH5188 powder

Composición química (peso %)
Elemento	C	Cr	Ni	Co	La	W	Si	Fe
Estándar	0.05~0.15	20.0~24.0	20.0~24.0	Bal.	0.03~0.12	13.0~16.0	0.2~0.5	≤3.0
typical	0.11	22.33	22.17	Bal.	0.06	14.91	0.44	0.49
Elemento	Mn	P	S	Cu	B	O	N
Estándar	≤1.25	≤0.02	≤0.015	≤0.070	≤0.015	≤0.030	≤0.030
typical	0.26	0.006	0.006	0.021	0.0092	0.017	0.01

 

GH5188	15~53μm Distribución del tamaño de las partículas			Caudal (seg. para 50 g)	Densidad aparente (g/cm3)	Densidad del grifo (g/cm3)
	D10	D50	D90
Estándar	15~25	30~40	50~60	≤25	≥4.55	≥5.30
typical	22.2μm	35.6μm	55.0μm	17	4.57	5.33

  3.Imágenes de la morfología SEM del polvo Imágenes de producción y pruebas:   4.Aplicación

• GH5188 has excellent formability, welding and other process properties, making it suitable for manufacturing parts for aircraft engines that require high strength below 980 ℃ and anti-oxidation below 1000 ℃. In the 1980s, GH5188 alloy was applied to components such as vortex plates and flame deflectors in turboshaft eight aircraft engines. Currently, some aircraft engines use GH5188 alloy sheets to prepare high-temperature components such as combustion chamber walls, outer walls, and sealing plates.