Sphärische Metallpulver Tantal (Ta)-Pulver
Produktcharakter：
The tantalum implant formed by 3D printing has the closest elastic modulus to human cartilage tissue, making it the most ideal orthopedic implant material. Spherical tantalum powder is suitable for processes such as laser/electron beam additive manufacturing, hot isostatic pressing, laser cladding, and hot/cold spraying.
| Markenname | Jinchun |
| Herkunft | China |
| Name des Produkts | Spherical Tantalum powder |
| Anmeldung | Orthopedic implants by 3d printing, laser/electron beam additive manufacturing, hot isostatic pressing, laser cladding, and hot/cold spraying |
| Form | Pulver |
| Farbe | Metal gray |
| Größe | 15~53μm, 53~150μm, 15~45μm, 45~106μm, 1~10μm, 5~25μm, or customized. |
| Standard | GB/T 19001-2016/ISO9001: 2015 |
| Reinheit | Ta: 99.95% min |
| Material | Ta |
| Verpacken | Vakuumverpackung |
PRODUKT DETAIL
PRODUKT DETAIL
Produkt Charakter
Spherical tantalum powder is manufactured using RF plasma spheroidization technology, which has the characteristics of high purity, low oxygen content, high sphericity, smooth surface, no satellites, uniform particle size distribution, excellent flowability, high loose density and tap density.
2.Spezifikation
Spherical Tantalum Powder
3 Bilder der SEM-Morphologie des Pulvers
Bilder von Produktion und Test:
4.Anwendung
| Chemische Zusammensetzung (wt.%) | ||||||||
| Element | Ta | Fe | Ni | Nb | W | Mo | Si | Ti |
| Standard | ≥99.95 | ≤0.002 | ≤0.001 | ≤0.001 | ≤0.010 | ≤0.0125 | ≤0.002 | ≤0.002 |
| typisch | ≥99.95 | 0.0013 | 0.0003 | 0.0005 | 0.001 | 0.001 | 0.002 | 0.0005 |
| Element | C | H | N | O(option 1) | O (option 2) | |||
| Standard | ≤0.030 | ≤0.050 | ||||||
| typisch | 0.0005 | 0.0008 | 0.002 | 0.01 | 0.042 | |||
| Spherical Tantalum powder | 15~53μm Partikelgrößenverteilung | Durchflussrate (sec. für 50 g) | Scheinbare Dichte (g/cm3) | Klopfdichte (g/cm3) | ||
| D10 | D50 | D90 | ||||
| Standard | 15~25 | 20~30 | 40~50 | ≤25 | ≥4.2 | ≥4.9 |
| typisch | 15.01μm | 28.81μm | 45.96μm | 5.98 | 9.61 | 10.8 |
| Spherical Tantalum powder | 53~150μm Partikelgrößenverteilung | Durchflussrate (sec. für 50 g) | Scheinbare Dichte (g/cm3) | Klopfdichte (g/cm3) | ||
| D10 | D50 | D90 | ||||
| Standard | 60~70 | 100~110 | 150~160 | ≤25 | ≥4.2 | ≥4.9 |
| typisch | 61.48μm | 104.9μm | 154.8μm | 4.8 | 7.58 | 9.2 |
Bilder von Produktion und Test:
4.Anwendung
- The tantalum implant formed by 3D printing has the closest elastic modulus to human cartilage tissue, making it the most ideal orthopedic implant material. Spherical tantalum powder is suitable for processes such as laser/electron beam additive manufacturing, hot isostatic pressing, laser cladding, and hot/cold spraying.